SIFAT FISIS MEKANIS PAPAN PARTIKEL DARI LIMBAH KAYU GERGAJIAN BERDASARKAN UKURAN PARTIKEL

Saibatul Hamdi, Arhamsyah Arhamsyah

Abstract


This research to exploit the waste sawdust of wood lua (Ficus glomerata ROXB) for the making particle board with the variation size measure particle that is 60 mesh, 80 mesh and mixture (60 mesh+80 mesh). Wood lua represent the wood less be recognized and to lower specific gravity. Agglutinant use the glue of Urea Formaldehyda (UF) with the glue concentration 20% from dry weight particle substance. The result of research show the average value board particle wood lua made for moisture content to range from 9,25-9,41%; wood density as 0,60-0,63 gr/cm3; thickness swelling as  9,13-9,53 %; modulus of rupture (MoR) 97,63-101,59 kgf/cm2; modulus of elasticity (MoE) 1,12-1,32.104 kgf/cm2; tensile strength as 2,96-3,99 kgf/ cm2. As a whole result examination  nature of fisis and mechanical particle board wood lua the standard quality of SNI 03-2105-2006 except for the examination modulus of elasticity (MoE).

Key wood : lua, fisis, mechanical, particle.


Full Text:

PDF

References


BSI, 2006. Papan Partikel. Standar Nasional Indonesia (SNI No. 03-2105-2006). Badan Standardisasi Indonesia. Jakarta.

Budiadji, 2004. Sifat Fisik dan Mekanis Papan Partikel Serabut Buah Kelapa Sawit ( Elais Guinensis Jack ) dengan Campuran Limbah Plastik Jenis PE ( Polyethlene ). Fakultas Kehutanan Unlam. Banjarbaru.

Firdaus, A. 2010. Pembuatan Alat Rotary Mixer Untuk Penggabungan Partikel Kayu Dengan Perekat. Laporan Penelitian Baristand Industri Banjarbaru.

Hamdi, 2009. Sifat Fisis Mekanis Papan Partikel dengan Variasi Ukuran Partikel, Jenis Kayu dan Jenis Perekat. Program Pasca Sarjana Fakultas Kehutanan Unlam Banjarbaru.

Jufriah, 2005. Sifat Fisika dan Mekanik Papan Partikel Dari Campuran Partikel Log Core Kayu Meranti Merah ( Shorea spp ) Dan Kayu Gmelina ( Gmelina arorea Roxb ). Prosiding Seminar Nasional Mapeki VIII. Tenggarong Kutai Kaltim.

Lelana, 2005. Pengawetan Bagian Lunak Kayu Kelapa Secara Rendaman Dingin Dengan Bahan Pengawet CCB, Info Hasil Hutan, Vol 11 No.2 Bogor.

Praguna, 2008. Sifat Fisik Dan Mekanik Papan Partikel Dari Limbah Plastik Jenis HDPE ( High Density Polyethylene ). Skripsi. Fakultas Kehutanan Unlam. Banjarbaru. Tidak Dipublikasikan.

Setyawati, 2003. Komposit Serbuk Kayu Plastik Daur Ulang: Teknologi Alternatif Pemanfaatan Limbah Kayu Dan Plastik, Program Pasca Sarjana/S3 IPB Bogor.

Sumardi I, 2004. Pengaruh Kerapatan Dan Ukuran Partikel Terhadap Sifat Fisis Dan Mekanis Papan Partikel Kayu Suren ( Toana sureni Merr ). Proceeding Mapeki VII, Makasar.

Suroto, 2007. Perbaikan Sifat Fisik Mekanik Dengan Teknik Pengempaan. Baristand Industri Banjarbaru.

………, 2009. Informasi Spesies Kayu Loa.( http;//www.plantamor.com ). Di Akses pada Tanggal 15 Juni 2009.




DOI: http://dx.doi.org/10.24111/jrihh.v2i2.1142

Refbacks

  • There are currently no refbacks.




JRIHH INDEXED BY :

       
       


Published by BARISTAND INDUSTRI BANJARBARU (E-ISSN: 2503-0779 dan P-ISSN : 2086-1400).

 Creative Commons License