GEL CASTING METHOD FOR COMPLEX-SHAPED DENSE CERAMIC FABRICATION

Ike Setyorini, Ria Julyana Manullang, Karlina Noordiningsih, Hernawan Hernawan

Abstract


The fabrication of complex-shaped dense ceramic has been done by gel casting method. Alumina was used as raw material in this study. Alumina was mixed with methacrylamide (MAM) dispersant and Methylenebisacrylamide (MBAM) monomer with a certain ratio until the suspension has a good ability to flow. Ammonium persulphate (APS) as an initiator and Tetra-methylethylene diamine (TEMED) as catalyst were added to accelerate the polymerization reaction. The suspension was then poured into wax mold, stayed until harden and burned at 1300 oC. The results showed the minimum viscosity of suspension is obtained with 80% alumina content and addition of dispersant at 0.15% weight of alumina. The addition of APS and TEMED at 0.2% weight of monomer solution and the addition of PEG at 1 µl per gram alumina provided the best mechanical strength of green body at 61.29 kg/cm2 . Addition of PEG was used to overcome the problem of lamination due to oxidation reactions by air

Keywords


gel casting, alumina, polymerization, dense ceramics, PEG

Full Text:

PDF

References


J.M. Tulliani dkk., Development and mechanical characterization of novel ceramic foams fabricated by gel-casting. J Eur Ceram Soc (2013)

J.Yang, J. Yu, Y. Huang. Recent developments in gelcasting of ceramics, Journal of the European Ceramic Society 31, 2569–2591, (2011)

SK. Swain, D.K. Segupta, B.P. Singh, S. Bhattacharjee. Gelcasting-A Versatile Process Part 1, International Ceramic Review , 54 (3): 174 -177, (2005)

SK. Swain, D.K. Segupta, B.P. Singh, S. Bhattacharjee. Gelcasting-A Versatile Process Part 2, International Ceramic Review, 54 (4): 252 – 257, (2005)

L. Sharifi, S.Ghanbarnezhad, S. Ghofran dan S. H. Mirhosseini, High Porous Alumina Bodies: Production and Properties via Gel-Casting Technique, International Journal of Advanced Science and Technology Vol.65. 59-70, (2014)

Y. Wang, dkk., Alumina ceramics via gelcasting forming with low-toxicity system, Advanced Materials Research Vols. 452-453, 35-40, (2012)

G.S. Koclar, Gelcasting of Alumina Ceramics With Gelatin and Carrageenan Gum and Investigation of Their Mechanical Properties, Thesis, Department of Chemical Engineering, İzmir Institute of Technology, 2013

Mingyue Huang, dkk., Fabrication and characterization of mini alumina ceramic turbine rotor using a tailored gelcasting process, Ceramics International 40, 7711–7722, (2014)

L. Montanaro, B. Coppola, P. Palmero dan J.M. Tulliani, A Review on Aqueous Gelcasting: a versatile and low-toxic technique to shape ceramics, Ceramics International, (2018)

Chang Gi Ha. Effect of Particle Size on Gel-Casting Process and Green Properties of Alumina. Thesis, Department of Material. Korea : Changwon National University, 2001

J.V.R. Kumar, H. N. Roopa and R. R Rao. Colloidal Processing and Gel Casting of Alumina. International Conference on Advanced Materials and Composites. Trivandrum, 24 – 26 Oktober: National Institute for Interdisciplinary Science & Technology (2007)

S. Dhara, R K Kamboj, M Pradhan dan P. Bhargava. Shape forming of ceramics via gelcasting of aqueous particulate slurries, Bull. Mater. Sci., 25 (6): 565-568, (2002)

Lei Yuan, dkk., Fabrication and characterization of Porous MgAl2O4 Ceramics via a novel aqueous Gel-Casting Process. Jurnal Materials 2017, 10, 1376, (2017)

Jia-Min Wu, Xiao-Yan Zhang, Jin-Long Yang. 2014. Novel porous Si3N4 ceramics prepared by aqueous gelcasting using Si3N4. Journal of the European Ceramic Society 34,1089–1096, (2014)

Jingtao Ma, Zhipeng Xie, Hezhuo Miao, Tibing Cheng. Improved Gelcasting, American Ceramic Society Bulletin, 82 (1): 54 – 58, (2003)

E.M.E. Ewais, Rheological properties of concentrated alumina slurries: influence of pH and dispersant agent. TESCE, 30 (2) : 891 – 912, (2004)

Y. Hirata, A. Nishimoto dan Y. Ishihara. Effect of Addition of Polyacrilic Ammonium on Colloidal Processing of α-Alumina, Journal of the Ceramic Society of Japan, 100 (8): 983-990, (1992)

Q.Shang, dkk., Gel-tape-casting of aluminum nitride ceramics. Journal of Advanced Ceramics, 6(1): 67–72 (2017)




DOI: http://dx.doi.org/10.32537/jkgi.v28i1.5406

Refbacks

  • There are currently no refbacks.



JKGI Google Scholar Link



Lisensi Creative Commons
Ciptaan disebarluaskan di bawah Lisensi Creative Commons Atribusi-NonKomersial-BerbagiSerupa 4.0 Internasional.