KARAKTERISTIK VULKANISASI KOMPON PADA PEMBUATAN WIPER BLADE

Abstract

The research aimed to study the effect of temperature and Hydrocxilamin Netral Sulphat (HNS)  to characteristics of vulcanization wiper blade. Temperature vulcanization used for the research was varied at 130 ^oC, 150 ^oC, 170 ^oC and Hydrocxilamin Netral Sulphat (HNS) at 5 phr, 10 phr. The result show that the effect temperature of vulcanization and Hydrocxilamin Netral Sulphat (HNS) consentration had significant effect on the scorch time (ts₂), optimum cure time (t₉₀), vulcanization rate, and modulus torsi (t) rubber compound wiper blade. The best treatment was found to be the T₂H₂(the addition of temperature 150 ^oC and HNS 10 phr) with characteristic of vulcanization wiper blade compound of 2,25 minute for the scorch time, 4 minute for the optimum cure time, 12, 12 minute for the vulcanization rate and 82kg.cm for the torcy modulus.